Dimension conversion

Magnetic flux density B and magnetic polarization J

IN TO BE MULTIPLIED BY TO OBTAIN
T = Wb/m2 = Vs/m2 10-4 Wb/cm2 = Vs/cm2
T 104 G
T 6.45 * 104 lines/square inch
Vs/cm2 104 T
G 10-4 T
lines/square inch 1.55 * 10-5 T

Magnetic field strength H

IN TO BE MULTIPLIED BY TO OBTAIN
A/m 0.01 A/cm
A/m 0.01257 Oe
A/m 0.0254 Ampere-turns/inch
A/cm 100 A/m
Oe 79.6 A/m
Ampere-turns/inch 39.37 A/m

Total core loss Ps

IN TO BE MULTIPLIED BY TO OBTAIN
W/kg 0.4536 W/lb
W/lb 2.205 W/kg

Length L

IN TO BE MULTIPLIED BY TO OBTAIN
cm 0.3937 inch
inch 2.54 cm

Area A

IN TO BE MULTIPLIED BY TO OBTAIN
cm2 0.155 square inch
square inch 6.45 cm2

Volume V

IN TO BE MULTIPLIED BY TO OBTAIN
cm3 0.061 cubic inch
cubic inch 16.4 cm3

Mass m

IN TO BE MULTIPLIED BY TO OBTAIN
g 0.0353 ounce
kg 2.20462 pound
ounce 28.35 g
pound 0.4536 kg

Force F

IN TO BE MULTIPLIED BY TO OBTAIN
N = kgm/s2 0.102 kp
kp 9.81 N = kg m/s2

Tensile strength Re, Rp, Rm

IN TO BE MULTIPLIED BY TO OBTAIN
N/mm2 0.102 kp/mm2
N/mm2 145 pounds/square inch (psi)
kp/mm2 9.81 N/mm2
pounds/square inch (psi) 6.90 * 10-3 N/mm2

Temperature T

IN TO BE MULTIPLIED BY TO OBTAIN
°C x 1.8 + 32 °F
°F x 0.556 - 17.8 °C