Umrechnungstabelle
Fläche A
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| cm2 | 0,155 | square inch |
| square inch | 6,45 | cm2 |
Kraft F
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| kp | 9,81 | N = kg m/s2 |
| N = kg m/s2 | 0,102 | kp |
Länge L
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| cm | 0,3937 | inch |
| inch | 2,54 | cm |
Magnetische Feldstärke H
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| Ampere-turns/inch | 39,37 | A/m |
| A/cm | 100 | A/m |
| A/m | 0,01257 | Oe |
| A/m | 0,01 | A/cm |
| A/m | 0,0254 | Ampere-turns/inch |
| Oe | 79,6 | A/m |
Magnetische Flussdichte B bzw. Magnetische Polarisation J
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| G | 10-4 | T |
| lines/square inch | 1,55 * 10-5 | T |
| T = Wb/m2 = Vs/m2 | 10-4 | Wb/cm2 = Vs/cm2 |
| T | 104 | G |
| T | 6,45 * 104 | lines/square inch |
| Vs/cm2 | 104 | T |
Masse m
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| g | 0,0353 | ounce |
| kg | 2,205 | pound |
| ounce | 28,35 | g |
| pound | 0,4536 | kg |
Ummagnetisierungsverlust Ps
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| W/kg | 0,4536 | W/lb |
| W/lb | 2,205 | W/kg |
Temperatur T
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| °C | x 1,8 + 32 | °F |
| °F | x 0,556 - 17,8 | °C |
Festigkeit Re, Rp, Rm
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| kp/mm2 | 9,81 | N/mm2 |
| N/mm2 | 0,102 | kp/mm2 |
| N/mm2 | 145 | pounds/square inch (psi) |
| psi | 6,90 * 10-3 | N/mm2 |
Volumen V
| IN | IST ZU MULTIPLIZIEREN MIT | UM ZU ERHALTEN |
|---|---|---|
| cm3 | 0,061 | cubic inch |
| cubic inch | 16,4 | cm3 |