Typical physical properties
| RESIDUAL CURVATURE (HORIZONTAL METHOD) | |
|---|---|
| Max. curvature for a strip section of 500 mm length for application widths > 150 mm | 17.5 mm |
| DEVIATION FROM THE SHEARING LINE (INTERNAL STRESSES) | |
|---|---|
| From 1,000 mm length for application widths > 500 mm | 1.0 mm |
| BURR HEIGHT (FOR SLIT WIDTH) | |
|---|---|
| Max. burr height | 0.025 mm |
| TENSILE STRENGTH Rm | |
|---|---|
| Longitudinal in rolling direction | 330 – 370 MPa |
| Transverse to rolling direction | 390 – 420 MPa |
| ULTIMATE YIELD STRENGHTH Rp 0,2 | |
|---|---|
| Longitudinal in rolling direction | 300 – 340 MPa |
| Transverse to rolling direction | 330 – 360 MPa |
| Saturation polarization Js | 2.03 T |
| Coercive field strength Hs | 5A/m |
| Curie temperature Tc | 745 °C/1,345 °F |
| Specific resistance Pe | 0.48 µΩm |
| Density Pm | 7.65 kg/dm3 |
| EDGE CAMBER | |
|---|---|
| Max. edge curvature within a strip section of 1,000 mm length for application widths > 150 mm | 0.5 mm |
| EDGE WAVE (WAVE FACTOR) | |
|---|---|
| Max. flatness for cut widths > 150 mm | 1.5 % |
| ELONGATION AT BREAK Al=80 | |
|---|---|
| Longitudinal in rolling direction | 6 – 14 % |
| Transverse to rolling direction | 24 – 48 % |
| HARDNESS | |
|---|---|
| HRB 15T | 75 – 85 |
| HV0.1 | 185 – 200 |
| STACKING FACTOR, DENSITY | |
|---|---|
| 0.20 mm | 95.0 % |
| 0.23 mm | 95.5 % |
| 0.27 mm | 96.0 % |
| 0.30 mm | 96.5 % |
| 0.35 mm | 97.0 % |
All test methods for thickness and width according to EN 10107 and IEC 60404-8-7.
All other test methods and definitions according to EN 10251 and IEC 60404-9.
Other properties and tolerances on request.